Name | Duplex washer |
Standard | DIN125A/DIN9021/DIN434,ISO7089/ISO7093,ASME B 18.22.1 |
Size Range | M5-M100 or non-standard as requested |
Finish | Bright&Clean |
Marking | HT&FST or customization |
Material | Duplex 2205 & Super duplex 2507 & S32760 |
Grade | Grade HV200 |
Certificates | EN10204-3.1B |
Non-standards | OEM is available, according to drawing or samples |
Samples | Samples available |
Package | Bulk in box and then in cartons, then on pallets, or according to customers' requirement. |
Payment | T/T,Western Union |
Duplex 2205
UNS | ID | JIS | W.Nr |
| S31803 | F51 | SUS32953L | 1.4462 |
Chemical composition of duplex 2205
| Alloy | % | Ni | Cr | Fe | Mo | N | C | Mn | Si | S | P |
| Duplex 2205 | Min. | 4.5 | 21 | margin | 2.5 | 0.08 | |||||
| Min. | 6.5 | 23 | 3.5 | 0.2 | 0.03 | 2 | 1 | 0.02 | 0.03 |
Minimum mechanical properties of duplex 2205 alloy at room temperature
| Tensile strength Rm N/mm2 | Yield strength RP0.2 N/mm2 | Elongation rate A5% | Brinell hardness HB |
| 620 | 450 | 25 | 290 |
Super Duplex 2507
UNS | ID | AISI/ASTM | W.Nr |
| S32750 | F53 | 2507 | 1.4410 |
Chemical composition of Super Duplex 2507
| Alloy | % | Ni | Cr | Mo | N | C | Mn | Si | S | P | Cu |
| 2507 | Min. | 6.0 | 24 | 3.0 | 0.24 | 0.08 | |||||
| Min. | 8.0 | 26 | 5.0 | 0.32 | 0.03 | 1.2 | 0.08 | 0.02 | 0.035 | 0.5 |
Minimum mechanical properties of alloy for Super Duplex 2507 at room temperature
| Tensile strength Rm N/mm2 | Yield strength RP0.2 N/mm2 | Elongation rate A5% | Brinell hardness HB |
| 800 | 550 | 15 | 310 |
Super Duplex S32760
UNS | ID | W.Nr |
| S32760 | F55 | 1.4501 |
Chemical composition of Super Duplex S32760
| Alloy | % | Ni | Cr | Mo | N | C | Mn | Si | S | P | Cu | W |
| F55 | Min. | 6.0 | 24 | 3.0 | 0.2 | |||||||
| Min. | 8.0 | 26 | 4.0 | 0.3 | 0.03 | 1.0 | 1.0 | 0.01 | 0.03 | 1.0 | 1.0 |
Minimum mechanical properties of Super Duplex S32760 alloy at room temperature
| Tensile strength Rm N/mm2 | Yield strength RP0.2 N/mm2 | Elongation rate A5% |
| 820 | 550 | 25 |
Name | Duplex washer |
Standard | DIN125A/DIN9021/DIN434,ISO7089/ISO7093,ASME B 18.22.1 |
Size Range | M5-M100 or non-standard as requested |
Finish | Bright&Clean |
Marking | HT&FST or customization |
Material | Duplex 2205 & Super duplex 2507 & S32760 |
Grade | Grade HV200 |
Certificates | EN10204-3.1B |
Non-standards | OEM is available, according to drawing or samples |
Samples | Samples available |
Package | Bulk in box and then in cartons, then on pallets, or according to customers' requirement. |
Payment | T/T,Western Union |
Duplex 2205
UNS | ID | JIS | W.Nr |
| S31803 | F51 | SUS32953L | 1.4462 |
Chemical composition of duplex 2205
| Alloy | % | Ni | Cr | Fe | Mo | N | C | Mn | Si | S | P |
| Duplex 2205 | Min. | 4.5 | 21 | margin | 2.5 | 0.08 | |||||
| Min. | 6.5 | 23 | 3.5 | 0.2 | 0.03 | 2 | 1 | 0.02 | 0.03 |
Minimum mechanical properties of duplex 2205 alloy at room temperature
| Tensile strength Rm N/mm2 | Yield strength RP0.2 N/mm2 | Elongation rate A5% | Brinell hardness HB |
| 620 | 450 | 25 | 290 |
Super Duplex 2507
UNS | ID | AISI/ASTM | W.Nr |
| S32750 | F53 | 2507 | 1.4410 |
Chemical composition of Super Duplex 2507
| Alloy | % | Ni | Cr | Mo | N | C | Mn | Si | S | P | Cu |
| 2507 | Min. | 6.0 | 24 | 3.0 | 0.24 | 0.08 | |||||
| Min. | 8.0 | 26 | 5.0 | 0.32 | 0.03 | 1.2 | 0.08 | 0.02 | 0.035 | 0.5 |
Minimum mechanical properties of alloy for Super Duplex 2507 at room temperature
| Tensile strength Rm N/mm2 | Yield strength RP0.2 N/mm2 | Elongation rate A5% | Brinell hardness HB |
| 800 | 550 | 15 | 310 |
Super Duplex S32760
UNS | ID | W.Nr |
| S32760 | F55 | 1.4501 |
Chemical composition of Super Duplex S32760
| Alloy | % | Ni | Cr | Mo | N | C | Mn | Si | S | P | Cu | W |
| F55 | Min. | 6.0 | 24 | 3.0 | 0.2 | |||||||
| Min. | 8.0 | 26 | 4.0 | 0.3 | 0.03 | 1.0 | 1.0 | 0.01 | 0.03 | 1.0 | 1.0 |
Minimum mechanical properties of Super Duplex S32760 alloy at room temperature
| Tensile strength Rm N/mm2 | Yield strength RP0.2 N/mm2 | Elongation rate A5% |
| 820 | 550 | 25 |